SHINY GOLD LIQUID 10%

OR10

Packaging by Price per kg Prices VAT incl. Quantity
5GR 0.005 13 435,20 € 67,18 €
20GR 0.02 11 195,40 € 223,91 €
100GR 0.1 10 662,36 € 1 066,24 €

Gold to appliance with brush

Groupe I

Firing temperature: 650-750°C

More info

 

Liquid gold & platinum

The liquid gold and liquid platinum are compositions containing different precious metals that will result in bright films with golden and silver/platinum shade

The gold and platinum can be applied either on porcelain, bone china, majolica, tiles and glass.

 

APPLICATION METHOD:

  1. Application of the gold or platinum:
    1. Brush: Put the liquid from the bottle into a small container. Deep a brush into the liquid and apply the product on the substrate to be decorated. If the product is too viscous (thick), add the diluent D 75 and mix it with the same brush. Keep adding the diluent until the desired viscosity, but do not add more than 5% of it.
    2. Spray: Put the liquid from the bottle into the reservoir of the spraying gun. Apply the product keeping a distance of 15 - 20 cm. If the product is not going through the spraying gun or dripping after spraying on the substrate, remove it from the reservoir and bottle and place it into a container. Add the diluent D 74 to reduce the viscosity and to apply a thinner layer of material (more transparent color). If the color is too weak, apply more times the product with the spray trying to avoid dripping of the product.
  2. Firing of the decorated piece:
    1. Glass: After decorating the piece, place it in the kiln. The recommended firing temperature is 600 – 620 °C. There is not specific time to go from room temperature to the peak temperature. But between 30 min and 2 h is the standard time. Also, we recommend a soak time of 5-10 min, specially if the maximum firing temp is in the lower range (600 ºC)
    2. Porcelain, bone china and tiles: After decorating the piece, place it in the kiln. The recommended firing temperature is 780 – 840 °C. There is not specific time to go from room temperature to the peak temperature. But between 30 min and 2 h is the standard time. Also, keeping the maximum temperature for 5 – 15 min is desired, especially if the maximum firing temperature is in the lower range (780ºC).

Data sheet

Composition Without lead